TCL-MF ultra-low formaldehyde no-ironing resin(TCL-MF)
General Description
DP finish for cotton, linen, viscose, Tencel and its blended fabrics with chemical fibers. The fabric after treatment features good recovery, anti shrinking, and durability to washing, low strength loss, especially released formaldehyde ultra lower than 75ppm.
Technique Data
1. Composition: Special modified dimethylol dihydroxy ethylene urea
2. Properties
Appearance: weakly yellow light tran***rent liquid
PH value: 6-7 Free formaldehyde: �.5% Solubility: mixed with any ratio of water
Application methods
Dilute the resin and catalyst with water before application respectively, adding softener at last, stirring thoroughly, adjust working liquor to pH value 5-5.5 with HAc, for garment finish by immersion method, for fabric finish by padding method.
Padding method: TCL-MF resin 60-100 g/L
CZ-3 catalyst 20-25% ratio to resin
Softener moderate dosage
Twice dipping twice padding (pick up 70%)----85â„?stenter drying----curing at 155â„?for 3 minutes
Immersion method: TCL-MF resin 50-100 g/L
CZ-3 catalyst 20-25% ratio to resin
Softener: moderate dosage
Immersion (15-20 minutes)---water extraction (pick-up 70-80%)----drying (moisture regain 7-10%)----ironing---155 â„?curing for 4-7 minutes
Practical dosage depends on trials, treated fabric should have clean surface and acidic pH value.
Package
25Kg,125Kg/ per plastic barrel
Safety Notes Stored at room temperature, validity for 6 months.
Notes: Above listed information is confirmed through practice, but owing to different textile printing technics, please make sure one after experiment.
Limited warranty:
As the application conditions and methods of this product in practice are not controllable,we will not give any form of guarantee about the applicatablity, and not afford any occasional or attached lose,the only guarantee we give is that the product we provide is meet the Huancheng available specification. |